This is the G3914A recipe on Plainsman M340 test tiles. They were fired at cone 6 using the PLC6DS schedule. We tested them in four different caustic liquids (using the GLLE test), there is no sign of leaching on any of them. This recipe contains only 4% black stain, that is enough to stain the base GA6-B glaze to a jet black. The surface has a unique iridescence that is not found in any other glossy black we have used.

This picture has its own page with more detail, click here to see it.
Simulating a white-on-black oil-spot effect at cone 6 oxidation proved to be a matter of repeated testing (that got me past some misconceptions). Stopping to think about the results at each step and keeping a good audit trail with pictures, in my account at insight-live.com, really helped. I had three black glazes: G2934BL satin (G2934 with black stain), G2926BB super-gloss (G2926B with black stain) and G3914A Alberta Slip black. Going on a hunch, I mixed up a bucket of the G3914A first (with some gum to help it survive second-coating without lifting). Rather than just try any white, I created G3912A by substituting as much CaO and MgO as possible for SrO in the G2934Y base. I later learned this to be an error, SrO reduces the surface tension, I should have used MgO (the G2934Y is a high-MgO glaze so it would have been fine as-is)! As you can see on the far right, this white still worked (at cone 5, 6, 7, 8). Why? There is another factor even more important. The effect only works on the Alberta Slip black. But its LOI is not higher than the others. And it worked even after ball milling. So I need to continue to work on this to learn more about why this works.

This picture has its own page with more detail, click here to see it.
We tested susceptibility to leaching of a stained glaze (top two) and another colored with raw metal oxides (bottom two) using the GLLE test (they were left overnight in vinegar and lemon juice). All the samples were fired using the C6DHSC firing schedule. The top two are G3914A (GA6-B Alberta Slip base with an addition of only 4% Mason 6600 black stain). There is no sign of leaching (Drano and bleach likewise did not affect it). The bottom two are G2926B transparent with 10% manganese dioxide and 5% copper oxide added (a common way to get black). The G2926B transparent base is proven, its surface shows no signs of gloss-loss in any testing we have done. But with manganese and copper added it is a very different story. Not only was this not nearly as black, but the vinegar and lemon juice matted and blued the top sections. Obviously, a ceramic stain added to the Alberta Slip GA6-B base is a far better way to make a leach-resistant black. Is it better than adding the black stain to G2926B? Yes, because far less is needed since the GA6-B base already has plenty of pigmentation.
![]() PayPal | No tracking, No ads, No paywall, No transient content! Just organized, concise information constantly updated and improved. Was this helpful? Consider supporting me. |
Buy me a coffee and we can talk